| 부식매질 | 성분 | 온도(℃) | 내식성 | |||
|---|---|---|---|---|---|---|
| 순수티타늄 | 지르코늄 | STS 316 | 하스텔로이 C | |||
| 수산화나트륨 (NaOH) | 30% | 30 | A | A | A | A |
| Boiling | A | A | B | B | ||
| 50% | 120 | A | A | B | B | |
| 80% | 170 | C | A | C | B | |
| 100% | 30 | A | A | |||
| 360 | C | B | C | |||
| 수산화칼륨 (KOH) | 10% | Boiling | A | A | A | A |
| 20% | Boiling | B | A | B | ||
| 50% | 30 | A | A | B | ||
| Boiling | C | A | B | B | ||
| 암모니아수 (NH4OH) | 10% | Boiling | A | A | A | A |
| 30% | 30 | A | A | A | A | |
| 수산화바륨 (Ba(OH)2) | 27% | 30 | B | A | C | A |
| 포화용액 | 30 | C | A | C | C | |
| 탄산칼륨 (K2CO3) | 20% | Boiling | A | A | A | A |
| 30% | Boiling | B | A | A | A | |
| 염소 (Cl2) | 100% dry gas (H2O less than 0.4%) | 30 | C | A | A | A |
| 100% dry gas (H2O less than 0.4%) | 30 | A | C | C | B | |
| 80 | A | C | C | B | ||
| 100% wet gas (H2O less than 0.95%) | 140 | A | C | C | ||
| 100% wet gas (H2O less than 1.5%) | 200 | A | C | C | ||
| 브롬 (Br2) | 100% Liquid Saturated water | 30 | C | C | ||
| 25 | A | C | ||||
| 과산화수소 (H2O2) | 6% | 30 | A | A | A | A |
| 30% | 30 | B | A | |||
| Boiling | A | |||||
| 50% | 60 | A | ||||
| 황 (S) | Suspension 100% molten condition | 30 | A | |||
| 240 | A | A | ||||
| 수은 (Hg) | 100% | 30 | A | |||
| 150 | B | |||||
| 100% (+ minute quantities Fe, Cu, Zn, Mg) | 370 | A | ||||
| 알루미늄 (Al) | 100% molten condition | 680 | C | |||
| 납 (Pb) | 100% molten condition | 600 | B | |||
| 950 | A | |||||
| 주석 (Sn) | 100% molten condition | 500 | A | |||
| 암모니아가스 (NH3) | 100% (14kg/cm2 pressure) 100% | 40 | A | A | ||
| 100 | A | A | ||||
The corrosion rate is under approximately 0.1mm/year and is almost completely corrosion resistant.
부식율 약 0.1m/year이하 이면, 완벽한 내식성을 가짐
The corrosion rate is approximately 0.1-1mm/year and may be used in cases where slight traces of corrosion are permitted.
부식율 약 0.1-1m/year이하 이면, 경미한 부식이 허락하는 부분에 사용 가능
The corrosion rate is in excess of approximately 1mm/year and is not suitable as an anti-corrosion material.
부식율 약 1m/year이하 이면, 반부식성 물질로 적합하지 않음.